Description
LUPOY HR5007A
Injection Molding Grade, PA/ABS
Heat Resistance, High Impact, High Flow
Application: Automotive Interior, E&E Housing
Properites |
Test condition | Test Method | Unit |
Typical Value |
| Physical |
|
|
|
|
| Specific Gravity |
|
ISO 1183 |
g/cm³
|
1.13 |
| Molding Shrinkage |
|
ISO 294-4 | % | 0.5-0.8 |
| Melt Flow Index |
250℃ 260℃ / 5kg |
ISO 1133 |
g/10min
|
25 |
| Mechanical |
|
|
|
|
|
Tensile Strength
@ Yield
|
50mm/min |
ISO 527 |
Mpa | 49 |
|
Tensile Elongation
@ Break
|
50mm/min |
ISO 527 |
Mpa | 90 |
|
Tensile Modulus
|
1mm/min | ISO 527 | Mpa | 2,500 |
|
Flexural Strength Flexural Modulus |
2mm/min 2mm/min |
ISO 178 ISO 178 |
Mpa Mpa |
80 2,280 |
| Charpy Impact Strength |
23℃
-30℃
|
ISO 179 |
KJ/m²
KJ/m²
|
NB NB |
|
Charpy Impact Strength (Notched) |
23℃
-30℃
|
ISO 179 |
KJ/m²
KJ/m²
|
52 22 |
|
IZOD Impact Strength, 4.0mm (Notched) |
23℃
-30℃
|
ISO 180 |
KJ/m²
KJ/m²
|
46 22 |
| Thermal |
|
|
|
|
|
Heat Deflection Temperature 4.0mm
(Unannealed, Flatwise)
|
1.8Mpa 0.45Mpa |
ISO 75
|
℃
|
109 |
| Vicat Softening Temperature |
5daN, 50℃/h
|
ISO 306 |
℃ |
128 |
|
Coefficient of Linear Thermal Expansion Flow Cross-flow |
|
ISO 11359-2 |
10-5 m/m℃
10-5 m/m℃
|
7.7E-05 8.3E-05 |
|
Flammability HB |
|
UL94 |
Thickness mm |
1.6, 3.0 |
|
Relative Temperature Index Electrical Mechanical with Impact Mechanical |
|
UL 746B |
℃ ℃ ℃ |
60 60 60 |
Processing Guide (Injection Molding)
Front
Cylinder Temperature Middle
Rear
℃
℃
℃
240 ~ 270
240 ~ 275
240 ~ 275
Processing Parameters
Unit
Value
Drying Temperature
℃
80-100
Drying Time
hrs
4-6
Maximum Moisture Content
%
0.02
Melt Temperature
℃
250-275
Nozzle Temperature
℃
245~275
Mold Temperature
℃
50~70
Back Pressure
kg/cm2
10 ~ 40
Screw Speed
rpm
40~70